3DPrinting
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: [email protected] or [email protected]
There are CAD communities available at: [email protected] or [email protected]
Rules
-
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
-
Be respectful, especially when disagreeing. Everyone should feel welcome here.
-
No porn (NSFW prints are acceptable but must be marked NSFW)
-
No Ads / Spamming / Guerrilla Marketing
-
Do not create links to reddit
-
If you see an issue please flag it
-
No guns
-
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe/ may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is 
Moderation policy: Light, mostly invisible
view the rest of the comments
Esteps and extrusion multiplier are related, but different, solutions to a similar problem. Changing one value by say 10% should be the same as changing the other by 10%.
Esteps is "how far does the extruder motor have to turn to extrude some length of filament". This lets your slicer know how much plastic volume should be extruded per step of your extruder motor
Flow rate is "crap, different filaments expand/contract at different rates and have different physical characteristics like viscosity".
This is why the extrusion multiplier setting is associated to your filament profile in PrusaSlicer and all its derivatives. I use a much lower value for ASA (around 0.88 if going slower and cooler) than PETG (0.95 ish) than PLA (1.0) than TPU (1.15 if memory serves).
I'll also tweak my extrusion multiplier depending on how I'm printing. For example, right now I have an ASA print going. The printer is laying down filament at 30 mm^3/s. To do this I'm printing a bit hotter than I normally would with this filament (245 vs 230). I'm also at 0.92 EM vs my usual 0.88.