this post was submitted on 22 Oct 2024
15 points (94.1% liked)
PocketKNIFE
1011 readers
1 users here now
This is the place for talking about all things pocket knives, and knife adjacent things. Folders large and small, multi-tools, sharpeners, even fixed blade knives are welcome. Reviews! Advice! Show off your Knives!
Also home of the incredibly loquacious Weird Knife Wednesday feature.
Simple Rules
- Don't be an asshole.
- Post any bigotry or hate speech and we'll cut you.
- No gore or injury posts.
- Keep politics out of here, unless it's knife related.
- Brand/model/maker/etc. elitism is highly frowned upon.
- Shilling your brand or product is OK provided that's not all you do and you make other contributions.
- For sale and trade posts allowed, but site admins and mods are not responsible for the outcome.
founded 1 year ago
MODERATORS
you are viewing a single comment's thread
view the rest of the comments
view the rest of the comments
Honestly? Don't use belt sharpeners, they fuck the metal up at the very edge. I'll explain more if you want, but people turn into assholes about the subject, so I don't go deeper without an invitation to do so.
That being said, what you're dealing with is a burr.
When you sharpen a knife on anything the very edge gets bent over a little. It kinda rolls, and that's what is behind a knife being sharp on one side and not another.
Doesn't matter what the angle is, what the surface is, it's about the physics involved in using abrasives and pressure on steel (or other metals). You can't avoid building a burr, so you don't try to. Instead, you work with it.
Since you're using a grinder, you can't use the usual method of "stropping" where you use the stone itself to gradually thin out and remove the burr (which, at a small enough scale, there's still some burr left).
So you'll have to actually strop, unless you have a stone handy. Any piece of leather will do because you don't need abrasive for this. I say that because they're are traces of silicates in leather, and some hides have more than others, so people tend to think you have țo strop om a leather that's more gritty. All you have to do is alternate running the blade from spine to edge across the leather on each side. This "wiggles" the burr until it snaps off, leaving a more even edge.
Most of the time, people get hung up on the angle being precise and even across the length of the blade and think that's the problem with their results. It very rarely is because the exact angle doesn't matter at all past a fairly obtuse angle (anything where the angle of the edge with both sides taken into account is less than about 45 degrees). It's a little less rare that it's the angle being the same along the edge because as long as the actual edge, the very tippy tip sharp part is even, the rest only matters in terms of how easy it will get through material that's thicker.
Consistent edges help cutting, but they aren't essential to sharpness or keenness.
Sharpness is the degree of angle behind the actual cutting edge, and keenness is how thin that cutting edge is. When you look at edges under a microscope, the difference is more discernable than with the naked eye (and the site knifesteelnerds can show you such images, and links to others). What it amounts to is that it doesn't matter what angle you sharpen at, or what you use to get that angle, what matters is that microscopic edge and how thin it is and how even it is.
So, with a belt grinder, use faster passes across the belt, use mild to soft pressure, and deburr once your angle is set.
You can test for a burr visually, but it's easier to run a fingernail from the spine of the blade down to the edge, on each side. The side with the burr is going to catch the fingernail. But you can't just strop that side. You gotta do both because that burr can switch sides. You actually want it to, because that gets it to come off, leaving the edge as clean as it gets.
Again, don't worry about the edges being even per se. That's only really important in details of use, not in getting a good cutting edge. A good cutting edge is about that microscopic edge being relatively even and as thin as possible.
Please do! Even though a lot of it may end up going way over my head, I'm always eager to learn more.
As for the burr, I've definitely been able to feel it catch on my finger once I've built it up. The way I've been doing it is a few passes with the medium belt (P220) until I've got a nice burr formed, and then a few passes with the fine (6000) to refine it until I can no longer feel any burr. Would I still need to look into stropping the blade after the fine belt's knocked off the burr? Or do I likely still have a burr that I just can't feel anymore that's still giving me trouble?
I think I might need to pick up a jeweler's loupe or something so I can get a better look at the actual edge and see.
Well, the key to belt sanders causing problems is heat. You've got abrasives scratching metal at high speed.
That's a lot of friction on a very small area. That friction on a bigger piece of metal is no big deal. But a knife edge gets very thin indeed. It simply can't take the heat being generated at the edge and move it into the rest of the knife fast enough to prevent the edge, perhaps a few millimeters worth, from getting too hot.
This results in the heat treatment of the steel being undone. The little crystals of iron, carbon, and whatever alloying metals are present come apart from their neat little stacks and get disordered. The metal that's left is more randomly arranged, so you can end up with very brittle (easy to break) or very soft (easy to deform) metal instead of what you started with.
Now, it's only maybe half the width of a pencil lead at most, but that's happening on the part of the knife that you rely on to cut things. It won't stop cutting, but what happens is that it gets dull much faster than it otherwise would. This means that your knife not only wont last, but it needs sharpening sooner, which reduces the life of the knife.
By the time you would feel any heat, it's too late. There are ways to mitigate that to some degree, but most people aren't set up to water cool their sanders/grinders.
As far as the burr goes, there's absolutely one still there. That's the only thing that will cause one side of a knife to be duller than the other. The little V of a knife that is the edge, when the burr is absent, will always cut in either direction approximately equal. Equal enough that you'd have to do some very sensitive testing to tell the difference, and even that won't be there on a theoretically perfectly formed edge.
You simply can't remove a burr on a running belt. No matter how fine the grit, the speed involved curls the side away from the belt. Now, you could stop the belt, and use very low pressure strokes to remove the burr on that surface. Same as with a stone in that regard.
I can't recall which model you said in the post, but most of the ones I've either used or seen used wouldn't be my top pick up deburr on, but it should be doable as long as you go slow and the device is stable.
Unlike stropping on a piece of leather though, you do the movement with the edge leading, just like you would if sharpening on a stone. But you do it at a wider angle, and with the gentlest amount of pressure possible as you go. You're wanting to mostly wiggle the burr without also doing much material removal as you go. There's always some material removed, but with a light enough touch, it won't be enough to cause an even smaller burr.
Tbh, I stopped using leather strops at all years ago based on some of the microscope images and videos that got shared at r/sharpening on reddit. Doing it on the stone is just faster and easier once you get a feel for the degree of pressure needed. So, if you can position things right to give you a stable surface to use, no need to mess with a dedicated strop, assuming you'll keep using the belt grinder. I've had to improvise sharpening on sandpaper before, which is essentially the same thing, and you can definitely deburr on that kind of surface.
And, I agree, a loupe, or other magnifier that can get you to enough magnification to see the scratch pattern on the edge is a major plus. I had a usb microscope I was using for a while, and it's lowest setting was 50×, and that was plenty for checking a burr. Overkill tbh. So a loupe should be about perfect.
Fwiw, all of this stuff I'm talking about here, I picked up from knifesteelnerds, Scienceofsharp, and the guys at r/sharpening for the most part. The subreddit is essentially useless now, but there's info on it for how to access the discord server the really knowledgeable guys migrated to.